Product Introduction
Grade 316L is the standard molybdenum-bearing grade, second in importance to 304 amongst the austenitic stainless steels. The molybdenum gives 316L better overall corrosion resistant properties than Grade 304, particularly higher resistance to pitting and crevice corrosion in chloride environments.
The austenitic structure also gives these grades excellent toughness, even down to cryogenic temperatures.
Compared to chromium-nickel austenitic stainless steels, 316L stainless steel offers higher creep, stress to rupture and tensile strength at elevated temperatures.
Product introduction:
| Commodity | 316L hot rolled stainless steel sheet |
| Grade | 316L |
| Brand | TISCO ,BAOSTEEL,POSCO,JISCO,LISCO |
| Certification | SGS,BV,IQI,TUV,ISO,etc |
| Thickness | 3-120mm |
| Width | 1219,1500,2000mm or as per customers’ requirements |
| Length | 2000,3000,6000mm or as per customers’ requirements |
| Surface | No.1 |
| Standard | JIS,AISI,ASTM,GB,DIN |
| Delivery time | About 15 -30 days or based on the sales contract |
| MOQ | 1 Ton |
| Advantages | offers higher creep, stress to rupture and tensile strength at elevated temperatures. |
Chemical Composition:
| Grade | Chemical Composition (WT %) | ||||||
| Carbon | Manganese | Phosphorus | Sulfur | Silicon | Chromium | Nickel | |
| 316L | ≤ 0.03 | ≤ 2.00 | ≤ 0.045 | ≤ 0.030 | ≤ 1.00 | 16.0 to 18.0 | 12.0 to 15.0 |
Physical Property:
| Physical Property | |||||
| Tensile Strength（Mpa） | Yield Strength(Mpa) | Elongation(%) | / | Hardness(HV/HB) | Density |
| ≥480MPa | ≥175MPa | ≥40% | / | ≤200HV | 7.98g/cm3 |
Surface Finish: